The following is the Material properties, Chemical analysis and Alternative grades for GB 9439 HT150 Gray Cast Iron.
Material properties of GB 9439 HT150 Gray Cast Iron:
For ferritic plus pearlitic gray iron. Its casting performance is good, the process is simple, the casting stress is small, does not need the artificial aging treatment, has certain mechanical strength and good vibration reduction performance.
Applications of GB 9439 HT150 Gray Cast Iron:
Used for electric housing, water pump housing, machine bases, etc. It is employed to manufacture chemical machinery, such as pump shells, containers, towers, flanges, etc. Also be used in circular speed 6 ~ 12m/s belt pulleys in which the working pressure of tubes is not too high.
Chemical analysis of GB 9439 HT150 Grey Cast Iron (mass fraction)(%)
Grade |
Thickness
/mm |
C |
Si |
Mn |
P
≤ |
S
≤ |
HT150 |
<30
30~50
>50 |
3.3~3.5
3.2~3.5
3.2~3.5 |
2.0~2.4
1.9~2.3
1.8~2.2 |
0.5~0.8
0.5~0.8
0.6~0.9 |
0.2
0.2
0.2 |
0.12
0.12
0.12 |
As for normal grey iron, the chemical composition is not important comparatively. The iron foundries could adjust the compositions according to their experience as long as they could meet the physical and mechanical requirements.
Mechanical properties of separately cast samples (30 mm diameter) of GB 9439 HT150 Gray Cast Iron:
Mechanical properties |
Material No. |
HT-150 |
Tensile strength Rm/Mpa |
150-250 |
Proof stress Rp0.1/MPa |
98-165 |
Elongation at fracture A/% |
0.3-0.8 |
Compression strength δdb /MPa |
600 |
Compression yield point δd0.1/MPa |
195 |
Bending strength δdB/MPa |
250 |
Shear strength δaB/MPa |
170 |
Torsional strength TtB/MPa |
170 |
Modulus of Elasticity E/(k MPa) |
78-103 |
Poisson ratio μ |
0.26 |
Bending fatigue strength δbW/MPa |
70 |
Fatigue limit under reversed tension-compression stresses δzdW/MPa |
40 |
Fracture toughness KIC/MPa3/4 |
320 |
GB 9439 HT150 Grey Iron Castings Hardness:
Grey iron grade |
Hardness grade |
Hardness Range HBS |
Metallography |
HT150 |
H175 |
150~200 |
Ferrite + Pearlite |
Alternative names:
Gray Cast Iron HT150 (GB 9439), GG15 (DIN 1691), EN-GJL-150 (EN 1561), GRADE 150 (ISO 185), CLASS 20 (ASTM A48), CLASS 25 (ASTM A48), FC150 (JIS G5501), G15 (UNI 5007), FGL150 (NF A32-101), 150 (BS 1452), FG15 (UNF), FGG15 (NBN 830-01), T150 (AS 1830), T180 (AS 1830), O115 (SS 14 01), SJG150 (NS11 100)